Leveraging the unparalleled advantages of our group's high-performance carbon fiber materials and warp knitted fabrics, we proudly introduce our state-of-the-art high-precision carbon fiber multi-axial warp knitted fabric prepreg production line. Offering a fiber area weight range of 100-600g/m² and T300-T800 grade unidirectional or fabric prepreg production capabilities, we have established a fully standardized prepreg material system. Utilizing thermosetting epoxy resins with features like medium-temperature curing, flame retardancy, and rapid curing, our products are engineered to meet the highest quality and performance demands across diverse industries, including wind power, rail transit, automobile, aviation, sports goods, and more.
| Type | Fiber | Fiber area weight g/m² | Resin content % | Prepreg area weight g/m | Width mm |
| UD150 | HFC20-25K | 150±3 | 35±2 | 231±7 | 1000~1270 |
| UD200 | HFC20-25K | 200±4 | 35±2 | 308±9 | 1000~1270 |
| UD300 | HFC20-25K | 300±6 | 35±2 | 462±14 | 1000~1270 |
| PN300 | ±45°Biaxial carbon fiber warp knitted fabric | 300 | 45±2 | 555±20 | 1000~1270 |
| LT400 | 0°/90°carbon fiber warp knitted fabric | 400 | 45±2 | 733±21 | 1000~1270 |
| TW200 | Carbon fiber twill fabric | 200 | 42±2 | 345±11 | 1000~1270 |
| Note: The types shown in this table are representative , not all , and the specific specifications should be determined according to customer requirements. | |||||
Our products can maintain their optimal quality for up to a year when stored at -18ºC.
Shipped using refrigerated containers to ensure product integrity.
Leveraging the unparalleled advantages of our group's high-performance carbon fiber materials and warp knitted fabrics, we proudly introduce our state-of-the-art high-precision carbon fiber multi-axial warp knitted fabric prepreg production line. Offering a fiber area weight range of 100-600g/m² and T300-T800 grade unidirectional or fabric prepreg production capabilities, we have established a fully standardized prepreg material system. Utilizing thermosetting epoxy resins with features like medium-temperature curing, flame retardancy, and rapid curing, our products are engineered to meet the highest quality and performance demands across diverse industries, including wind power, rail transit, automobile, aviation, sports goods, and more.
| Type | Fiber | Fiber area weight g/m² | Resin content % | Prepreg area weight g/m | Width mm |
| UD150 | HFC20-25K | 150±3 | 35±2 | 231±7 | 1000~1270 |
| UD200 | HFC20-25K | 200±4 | 35±2 | 308±9 | 1000~1270 |
| UD300 | HFC20-25K | 300±6 | 35±2 | 462±14 | 1000~1270 |
| PN300 | ±45°Biaxial carbon fiber warp knitted fabric | 300 | 45±2 | 555±20 | 1000~1270 |
| LT400 | 0°/90°carbon fiber warp knitted fabric | 400 | 45±2 | 733±21 | 1000~1270 |
| TW200 | Carbon fiber twill fabric | 200 | 42±2 | 345±11 | 1000~1270 |
| Note: The types shown in this table are representative , not all , and the specific specifications should be determined according to customer requirements. | |||||
Our products can maintain their optimal quality for up to a year when stored at -18ºC.
Shipped using refrigerated containers to ensure product integrity. 