Introduction:
ELSE Rare earth PVB interlayer film is a macro molecule material which produced by extrusion using PVB resin, plasticizer and a special rare earth additives. With the rare earth additives ,our ELSEPVB film is not only with high visible transmittance, super anti-penetration but also with high Infrared Rejection Rate and Ultraviolet Rejection Rate can shield out the heat and sound. With the rare earth additives ,our RE film is not only with high visible transmittance, super anti-penetration but also with high Infrared Rejection Rate and Ultraviolet Rejection Rate can shield out the heat and sound. The rare earth metals in our RE film can easily insulate infrared and ultraviolet rays as we transform the nanoscale molecule structure of the metal. This structure targets the specific characteristics of infrared and ultraviolet light. Solar radiation heat energy is absorbed into the RE film surface and transformed into physical heat energy then is carried away by air convection.The major application of PVB film is laminated safety glass used on automotive windshields, architectural glass as well as the bullet proof glass.
Features:
High Visible Light Transmittance
High Infrared Rejection Rate
High Ultraviolet Rejection Rate
Application:
Laminated safety glass.
Automotive glass
Typical Specifications:
Test item | Unit | Standard | Value |
Appearance | / | / | blackish green |
Thickness | mm | / | 0.38 |
VA Content | % | analytical | 28 |
Melt index | g/10min | GB/T3682 | 5 |
Crosslinking rate | % | solvent extraction | ≥75 |
Water absorption (20ºC,24h) | % | GB/T1034 | ≤0.1 |
EVA/Glass peel strength | n/cm | GB/T2790 | ≥50 |
Anti-ultraviolet(ultraviolet 313nm,1000h) | / | IEC61345 | No bubbles, no cracking, no relaxation |
Anti-moisture and heat aging(85ºC,85%rh,1000h) | / | GB/T7141 | No bubbles, no cracking, no relaxation |
Heat resistance(+90ºC,1000h) | / | No bubbles, no cracking, no relaxation | |
Visible Light Transmission | % | / | 70 |
Infrared Rejection Rate | % | / | 85.6 |
Ultraviolet Rejection Rate | % | / | 96.6 |